Reasons for collapse and collapse after glass edging

  • Author:Fanyu
  • Source:Https://www.glass.com.cn
  • Release on:2019-03-21

After the glass is machined by the edger, if the collapse of the edge occurs, it will not only affect the aesthetics of the glass, but also affect the safety during use.

The reasons for chipping or chipping after edging of glass are mainly as follows.


1. The grinding amount of the glass is too large and the speed is too fast.

2. The amount of water is not enough.

3. The amount of glass grinding is unevenly distributed.

4, the grinding wheel is not sharp enough, the water pipe is blocked, the water temperature is too high, the splint is worn, and the chain is too long.

5, the original film has no bubbles, not seen, especially in the glass inside the stone, easy to break in the heating section, the skin is much better.

6. There is no crack in the glass edging or opening, and it is damaged in the heating section.

The solution is to adjust the amount of uniform grinding and water addition, and reduce the edging speed appropriately.